100%RTV Acetic Gp Clear Sealing Silicon Glass Silicone Sealant 1200 for Windows

• Customization: Available
• CAS No.: 63394-02-5
• Bonding Function: Liquid Sealing Leak
• Morphology: Glue
• Application: Construction
• Material: Silicone
• Classification: Room Curing
• Main Agent Composition: Rubber
• Characteristic: Waterproof
• Promoter Composition: Curing Agent
• Composition: Organic Material
• Color: Clear
• Transport Package: Carton Box
• Specification: 24pcs/ctn
• Trademark: GNS
• Origin: China
• HS Code: 35061000
• Production Capacity: 144000PCS/Day

Product Description

100%rtv Acetic gp Clear Sealing Silicon Glass Silicone Sealant 1200 for Windows

100%rtv Acetic gp Clear Sealing Silicon Glass Silicone Sealant 1200 for Windows is a cost effective, general purpose acetoxy cure silicone sealant which offers long term durability in a range of general sealing and general glazing applications. It can be used to glaze, seal and fill joints on windows, signs, internal fixtures and fitting like doors and so on.


FEATURES 

1. Easy to use - one part, no mixing required. Can be dispensed with an ordinary caulking gun.
2. Cures to a strong, flexible seal capable of withstanding movement in and around the joint.
3. No seasonal limited in application.
4. Outstanding weatherproofing ability, resisting to ultraviolet ray, ozone, snow, or temperature extremes.
5. Non-slumping; can be used in vertical and overhead joints.

PACKAGING
Available in: 
Standard Size:
270ml recyclable plastic cartridge, 24ctgs/ctn
Special Size:
Contact us for special size.
COLORS         
Available for four standard colors: Translucent, White, Black, Aluminum.
Contact us for special colors.
PERFORMANCE DATA

Test Parameter	Unit	Result
As Supplied Tested at 23ºC and 50% RH
Specific Gravity	g/ml	0.94±0.02
Flow (sag or slump)	mm	0
Extrusion Rate	ml/minute	130
Skin Time	minute	5~10
Tack-free Time	hour	≤1.0
Curing time (5mm)	hour	≤18
As Cured-after 21 days at 23ºC and 50% RH
Durometer Hardness, Shore A	Points	18
Movement Capability	%	±20
Tensile/Modulus at 50% Elongation	Mpa	0.28
Tensile/Modulus at 100% Elongation	Mpa	0.3
Ultimate Tensile Strength Ultimate Elongation at Break	Mpa %	0.4 375