Glass Silicone Sealant Sealants and Adhesives Anti-Fungus for Metal Materials

• Customization: Available
• CAS No.: 4253-34-3
• Formula: C3h8n2o
• Model NO.: G44
• EINECS: 230-391-5
• Bonding Function: Structural Adhesive
• Morphology: Paste
• Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing
• Material: Silicone
• Classification: Adhesive
• Main Agent Composition: Silicone
• Characteristic: Weatherability
• Promoter Composition: Adhesive
• Composition: Adhesive
• Color: White, Black, Clear
• Shelf Life: 12 Months
• Skin Time: 5mins
• Transport Package: Five Ply Master Carton
• Specification: 24 pcs in a carton
• Trademark: GNS
• Origin: China
• Production Capacity: 200000000

Product Description

 

GNS G44 TVS & BUTT JOINT SILICONE
 

GNS G44 TVS & BUTT JOINT SILICONE is an one part, high performance silicone sealant with ultimate tensile strength, mechanical properties for curtain wall, Total Vision System (TVS) and architectural applications. It has very good weathering resistance, durability, sealing and bonding properties.

 

 

FEATURES 

 

1. Acetoxy room temperature cure, easy to apply.
2. Outstanding weatherproofing ability, resisting to ultraviolet ray, ozone, snow, or temperature extremes.
3. Excellent adhesion to most building materials.
4. Seals water tight.

TYPICAL USE

1. General glazing and weather sealing in curtain wall and building facades.
2. EIFS, the non-structural curtain walls and building construction applications.
3. Window e.g.: vinyl windows, doors and perimeter joints.
4. Surface like glass, aluminium, ceramics, metals, steel, fiberglass, most plastics, tiles, bricks, marble & granite and so on.

PERFORMANCE DATA

Test Parameter	Unit	Result
As Supplied Tested at 23ºC and 50% RH
Flow (sag or slump)	mm	0
Extrusion Rate	ml/minute	130
Skin Time	minute	5~10
Tack-free Time	hour	≤1.0
Curing time (5mm)	hour	≤18
As Cured-after 21 days at 23ºC and 50% RH
Durometer Hardness, Shore A	Points	18
Movement Capability	%	±20
Tensile/Modulus at 50% Elongation	Mpa	0.28
Tensile/Modulus at 100% Elongation	Mpa	0.3
Ultimate Tensile Strength Ultimate Elongation at Break	Mpa %	0.4 375