860ml 1000g All Seasons Maximum Yield PU Foam Flexible Insulating and Acoustic

• Formula: Mixed
• Bonding Function: Structural Adhesive
• Application: Automobile, Construction, Woodworking, Packing
• Material: Polyurethane
• Classification: Room Curing
• Main Agent Composition: Natural Polymer
• Characteristic: Waterproof
• Promoter Composition: Curing Agent
• Composition: Organic Material
• Color: White
• OEM: Avaliable
• Curing System: Moisture-Cure
• Drying Time: Dust-Free After 20-25 Min
• Usage: Construction, Fiber & Garment, Footwear & Leather
• Supply Ability: 300000 Piece/Pieces Per Day
• Application Temper: Ture Range: +5°c~+35°c
• Yield (L): 31-36
• Adhesive Strengh(Kpa): >70
• Lead Time: 2~3 Weeks
• Shipping: Support Sea Freight
• Brand Name: Gns
• Shrink: None
• Feature: Very Good Filling Capacities
• Shelf Life: 12momth
• Transport Package: 750ml/Can, 500ml/Can, 12PCS/CTN
• Specification: Gross weight is 350g to 950g upon requested.
• Trademark: GNS
• Origin: China
• Production Capacity: 300000 Piece/Pieces Per Day

Product Description

GNS  65L MULTI-USE PU FOAM

GNS  65L  PU FOAM is a one-component, ready to use multi-purpose Polyurethane Foam. It is fitted with a plastic adapter head for use with a foam application gun or plastic applicator. The foam will expand and cure by moisture in the air. It is used for a wide range of building applications. It is very good for filling and sealing with excellent mounting capacities, high thermal and acoustical insulation.

PRODUCT FEATURES

1. Good adhesion to a wide variety of surfaces such as UPVC, masonry, brick, block work, glass, steel, aluminum, timber and other substrates (except PP, PE and Teflon);
2. Very good filling capacities;
3. Application temperature is between + 5ºC to +35ºC;
4. Optimal application temperature is between +18ºC to +30ºC;
5. It contains CFC-free propellants which are harmless to the ozone layer.

APPLICATIONS AREAS

1. Installing, fixing and insulating of door and window frames;
2. Filling and sealing of gaps, joint, openings and cavities;
3. Connecting of insulation materials and roof construction;
4. Bonding and mounting;
5. Insulating the electrical outlets and water pipes;
6. Heat preservation, cold and sound insulation;
7. Packaging purpose, wrap the precious & fragile commodity, shake-proof and anti-pressure.

APPLICATION INSTRUCTIONS

1. Shake the aerosol can for at least 40 seconds;
2. Clean and moisten surfaces with a water sprayer prior to application;
3. Fit the gun or plastic applicator on the adapter.
4. Firmly screw the can on the adapter and turn the flow adjustment screw; Fill the holes and cavities.
5. Bottom up during application; Foam will be tack-free in about 10 minutes; Excess can be trimmed in about one hour;
6. Fresh foam can be removed by using GNS Foam cleaner . Cured foam can only be removed mechanically.

STOREAGE AND SHELF LIFE
12 months in unopened packing store in temperature between +5ºC to +25ºC, Keep in cool, shade and well ventilated area. Always keep the can with the valve pointed upwards.

PACKAGING
750ml/can, 500ml/can,12pcs/ctn for both Manual type and Gun type.
Gross weight is 350g to 950g upon requested.

SAFETY RECOMMENDATION

1. Do not breathe spray/vapor; In case of eye contact, flush with water and get immediate medical attention;
2. Use in well-ventilated areas;
3. Wear suitable protective clothing, gloves and goggles;
4. Keep away from direct sunlight and do not expose temperatures over 50ºC;
5. Do not burn or pierce even after use;
6. Keep away from heat, sparks, flames and static electricity; Turn off sources of ignition (pilot light etc.);
7. Keep out of the reach of children.

TYPICAL PROPERTIES

Base	Polyurethane
Consistency	Stable Foam
Curing System	Moisture-cure
Tack-Free Time (min)	8~9
Drying Time	Dust-free after 13-15 min.
Cutting Time (min)	60~70(+25ºC)
Yield (L)	43
Shrink	None
Post Expansion	8%
Cellular Structure	>84% close cells
Specific Gravity (kg/m³)	19
Temperature Resistance	-50ºC~+80ºC
Application Temperature Range	+18ºC~+30ºC
Colour	white
Fire Class (DIN 4102 )	B3
Insulation Factor  (Mw/m.k)	0.039
Compressive Strength (kPa)	140
Tensile Strength (kPa)	200 (10%)
Adhesive Strength(kPa)	130
Water Absorption (ML)	2~3(no epidermis)
	<0.5(with epidermis)