Gns G22 General Purpose Acetoxy Silicone Sealant

• Customization: Available
• Application: Automobile, Construction, Packing, Woodworking
• Bonding Function: Structural Adhesive
• Model NO.: G22
• Color: White
• Composition: Organic Material
• Morphology: Paste
• Package: 12PCS/CTN, 24PCS/CTN, 25PCS/CTN, 30PCS/CTN
• Density: 0.93
• MOQ: 2000 PCS
• Skin Type: Acetoxy Cured
• CAS No.: 9009-54-5
• EINECS: 210-898-8
• Material: Silicone
• Classification: Room Curing
• Main Agent Composition: Silicone
• Characteristic: Weatherability
• Promoter Composition: Filler
• Transport Package: Carton
• Specification: 280ml, 300ml, 590ml
• Trademark: GNS
• Origin: China
• HS Code: 35061090
• Production Capacity: 96000 Pieces/Day

Product Description

GNS G22 GENERAL PURPOSE Acetoxy SILICONE SEALANT

GNS G22 GENERAL PURPOSE SILICONE SEALANT  is a cost effective, general purpose acetoxy cure silicone sealant which offers long term durability in a range of general sealing and general glazing applications. It can be used to glaze, seal and fill joints on windows, signs, internal fixtures and fitting like doors and so on.


FEATURES 

1. Acetoxy room temperature cure, easy to apply.

2. Outstanding weatherproofing ability, resisting to ultraviolet ray, ozone, snow, or temperature extremes.

3. Excellent adhesion to most building materials.

4. Seals water tight.

PACKAGING
Available in: 
Standard Size:
270ml/280ml/300ml recyclable plastic cartridge, 24ctgs/ctn
590ml/600ml Aluminum sausage, 20ssgs/ctn

COLORS         
Available for four standard colors: Translucent, White, Black, Aluminum.
Contact us for special colors.

PERFORMANCE DATA

Test Parameter	Unit	Result
As Supplied Tested at 23ºC and 50% RH
Specific Gravity	g/ml	0.94±0.02
Flow (sag or slump)	mm	0
Extrusion Rate	ml/minute	130
Skin Time	minute	5~10
Tack-free Time	hour	≤1.0
Curing time (5mm)	hour	≤18
As Cured-after 21 days at 23ºC and 50% RH
Durometer Hardness, Shore A	Points	18
Movement Capability	%	±20
Tensile/Modulus at 50% Elongation	Mpa	0.28
Tensile/Modulus at 100% Elongation	Mpa	0.3
Ultimate Tensile Strength Ultimate Elongation at Break	Mpa %	0.4 375