Neutral Cureweather Proof Silicone Sealant Non-Acidic Will Not Corrode Metal or Other Corrosion-Sensitive Material

• CAS No.: 63394-02-5
• Bonding Function: Liquid Sealing Leak
• Morphology: Glue
• Application: Construction
• Material: Silicone
• Classification: Room Curing
• Main Agent Composition: Rubber
• Characteristic: Waterproof
• Promoter Composition: Curing Agent
• Composition: Organic Material
• Color: Black
• Transport Package: Carton Box
• Specification: 24pcs/ctn
• Trademark: GNS
• Origin: China
• HS Code: 35061000
• Production Capacity: 144000PCS/Day

Product Description

Neutral cureweather proof silicone sealant non-acidic will not corrode metal or other corrosion-sensitive material

Neutral cureweather proof silicone sealant non-acidic will not corrode metal or other corrosion-sensitive material is a one part, neutral cure, high performance weather seal silicone sealant which exhibits outstanding physical properties for projects and general building constructions applications. It has excellent weathering resistance, sealing and primerless adhesive properties, durability, virtually unaffected by sunlight, rain, wind, frost, snow, air pollutant, ozone and temperature extremes.


FEATURES 

1. One part, can be easily used and extruded with common caulking guns.
2. Excellent adhesion to most construction materials without the primmer.
3. Outstanding weatherproofing ability, resisting to ultraviolet ray (UV), ozone, snow or temperature extremes.
4. Neutral cure, non-acidic, will not corrode metal or other corrosion-sensitive material.

TYPICAL USE

1. Aluminum composite panels cladding, aluminum and glass curtain walls.
2. General glazing and weather sealing in curtain walls and building facades.
3. Windows & doors perimeter joints. e.g. Vinyl windows, aluminum windows, PVC, UPVC windows etc.
4. Glass, aluminum, ceramics, metals, steel, fiberglass, most plastics, tiles, bricks, marble & granite surfaces and so on.

PERFORMANCE DATA

Test Parameter	Unit	Result                            Translucent          Pigmented
As Supplied Tested at 23ºC and 50% RH
Specific Gravity	g/ml	1.00±0.02	1.43±0.02
Flow (sag or slump)	mm	0	0
Extrusion Rate Skin Time	ml/minute minute	100 5~10	123 ≤80
Tack-free Time	hour	≤1	≤8
Curing time (5mm)	hour	≤12	≤15
As Cured-after 21 days at 23ºC and 50% RH
Durometer Hardness, Shore A	Points	28	36
Elastic Recovery	%	98	98
Movement Capability	%	±25	±40
Tensile/Modulus at 50% Elongation	Mpa	0.27	0.52
Tensile/Modulus at 100% Elongation	Mpa	0.35	0.68
Ultimate Tensile Strength Ultimate Elongation at Break	Mpa %	0.37 175	0.84 400