3L/4L/18L High Quality Mastic Granite Stone Glue Neutral Marble Silicon Adhesive For Marble
3L/4L/18L High Quality Mastic Granite Stone Glue Neutral Marble Silicon Adhesive For Marble is manufactured with high pureness, stable and high quality materials, and under meticulous and cautious management and control, which have high quality. It is used for binding and repairing of all kinds stone materials and mending of seams and dents of the surface of the stone products. It possesses the character of high intensity, fast curing, weatherproof, corrosion resistance and can be polished.
PRODUCT FEATURES
- Cure in short time
- Can be operated in cold weather (-10ºC~45ºC)
- High intensity, hard enough for polish
- No color change, cracking or shrinkage
- Weatherproof
- corrosion resistance
- High toughness after cured
APPLICATIONS AREAS
- Bonding and repairing of all kind of stones like marble, ceramics, and granite, so on.
- Fast fixing and pattern making
APPLICATION INSTRUCTIONS
- The surfaces must be clean and free from dust and grease
- Mix 100 parts of adhesive with 3 parts of hardener until a homogeneous mixture is obtained.
- Apply the mixture to the bonding area and hold it together about 3-5 minutes.
- Keep the assembled parts from moving during cure.
STOREAGE AND SHELF LIFE
12 months in unopened packing store in temperature between +5ºC to +25ºC, Keep in cool, shade and well ventilated area.
PACKAGING
18L/bucket, 4L/bucket (4buckets/ctn), 3L/bucket (6buckets/ctn), 0.6L/bucket(12buckets/ctn)
Gross weight is upon request.
Stand color: transparent, white, beige, black. More colors on demand.
SAFETY RECOMMENDATION
- Irritating to eyes and skin
- If eyes contact occurs, immediately flush eyes with plenty of water and consult doctor
- Use only in well-ventilated areas
- Mixing the components in correct ratio is critical since the amount of hardener affect working time
- Avoid contact with eyes. Keep non-cured adhesive away from children
TYPICAL PROPERTIES
Mix ratio
|
100 part adhesive with 3 part hardener |
| Working time |
3-10 min |
| Mixing Ratio |
3% |
| Bending modulus of elasticity |
≥2500MPa |
| Bending strength against Viscosity |
≥17.0MPa |
| Impact Strength |
≥2.5MPa |
Press shear strength
(stone-stone)
|
Stone-stone standard |
≥9 MPa |
| Heating process |
≥9 MPa |
| Hot Water soak process |
≥6 MPa |
| Alkali treatment |
≥6 MPa |
| Freezing and heating cycle treatment |
≥6 MPa |
Press shear strength
(stone-stainless steel) |
Stone-stainless steel standard |
≥9 MPa |