Waterproof General Purpose High Viscosity RTV Gp Neutral Corning Acetic Adhesive Silicone Sealant

• CAS No.: 63394-02-5
• Bonding Function: Liquid Sealing Leak
• Morphology: Glue
• Application: Construction
• Material: Silicone
• Classification: Room Curing
• Main Agent Composition: Rubber
• Characteristic: Waterproof
• Promoter Composition: Curing Agent
• Composition: Organic Material
• Color: Clear
• Transport Package: Carton Box
• Specification: 24pcs/ctn
• Trademark: GNS
• Origin: China
• HS Code: 35061000
• Production Capacity: 144000PCS/Day

Product Description

Waterproof general purpose high viscosity rtv gp neutral corning acetic adhesive silicone sealant

Waterproof general purpose high viscosity rtv gp neutral corning acetic adhesive silicone sealant is acetoxy cure, one part RTV silicone sealant. Can be applied on glass, ceramics vitreous enamels. shelves, counter cabinets, signs and many other building materials.


FEATURES 

1. Easy to use - one part, no mixing required. Can be dispensed with an ordinary caulking gun.
2. Cures to a strong, flexible seal capable of withstanding movement in and around the joint.
3. Excellent resistance to weathering, UV light, vibration, moisture, ozone, temperature extremes, airborne pollutants, cleaning detergents and many solvents.
4. Non-slumping; can be used in vertical and overhead joints.

PACKAGING
Available in: 
Standard Size:
270ml recyclable plastic cartridge, 24ctgs/ctn
Special Size:
Contact us for special size.
COLORS         
Available for four standard colors: Translucent, White, Black, Aluminum.
Contact us for special colors.
PERFORMANCE DATA

Test Parameter	Unit	Result
As Supplied Tested at 23ºC and 50% RH
Specific Gravity	g/ml	0.96±0.02
Flow (sag or slump)	mm	0
Extrusion Rate Skin Time	ml/minute minute	150 5~10
Tack-free Time	hour	≤1.0
Curing time (5mm)	hour	≤12
As Cured-after 21 days at 23ºC and 50% RH
Durometer Hardness, Shore A	Points	22
Movement Capability	%	±25
Tensile/Modulus at 50% Elongation	Mpa	0.24
Tensile/Modulus at 100% Elongation	Mpa	0.28
Ultimate Tensile Strength Ultimate Elongation at Break	Mpa %	0.32 250